ASTM A209, Speċifikazzjoni Standard għal Boiler tal-Karbonju-Molibdenu Alloy-Steel mingħajr saldatura u Tubi tas-Superheater.
OD: 10mm ~ 203mm
WT: 2.0mm~25mm
Tul: 5.8-12m jew kif meħtieġ mill-klijenti
Grad:ASTM A209 T1,ASTM A209 T1a,ASTM A209 T1b
Teknika: mingħajr saldatura
Użu:
1. Pipeline tat-trasport tal-fluwidu bi pressjoni baxxa u medja
2. Impjant tal-enerġija
3. Tubu tal-bojler
4. Industrija petrokimika
Pakkett: Żejt dipped jew wiċċ miżbugħ iswed, ippakkjat f'boroż li jifilħu għall-baħar, eżagonali miġbura.
Kompożizzjoni Kimika:
|
C |
Mn |
P |
S |
Si |
Mo |
|
|
T1 |
0.10-0.20 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1a |
0.15-0.25 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
|
T1b |
=0.14 |
0.30-0.80 |
=0.025 |
=0.025 |
0.10-0.50 |
0.44-0.65 |
Proprjetajiet mekkaniċi:
|
Grad |
T1 |
T1a |
T1b |
|
Qawwa tat-tensjoni min Ksi(Mpa) |
55(380) |
60(415) |
43(365) |
|
Qawwa tar-Rendiment Min Ksi(Mpa) |
30(205 |
32(220) |
28(195) |
|
Titwil f'2in jew 50mm min% |
30 |
30 |
30 |
Trattament bis-sħana:
Il-pajpijiet ipproċessati bis-sħana u pproċessati fil-kesħa għandhom jiġu ttrattati bis-sħana f'temperatura ta '650 grad? Għalinqas. Il-manifattur jista 'jagħżel ittemprar komplut, ittemprar iżotermali jew normalizzazzjoni flimkien ma' ittemprar. It-temperatura minima tat-tempra m'għandhiex tkun inqas minn 650 grad.