Rare earth has a strong chemical affinity with impurities such as oxygen and sulfur in molten steel. At steelmaking temperature (about 1873K), rare earth can react with impurities such as oxygen and sulfur in molten steel to form rare earth oxides, sulfides or oxysulfides. The deoxidation equilibrium constant or desulfurization equilibrium constant of these reactions is lower than or close to that of commonly used deoxidizers and desulfurizers. Therefore, rare earth steel additives can be used as strong deoxidizers and desulfurizers for molten steel to purify it. Commonly used rare earth steel additives are mainly mixed rare earth metals or high-grade (RE>27%) ligi tal-ferrosilicon tal-art rari, u xi kultant jintużaw ukoll ossidi tal-art rari b'aġenti li jnaqqsu mħallta.
Ossidi, sulfidi jew oxysulfides iġġenerati mir-reazzjoni ta 'art rari ma' ossiġnu u kubrit fl-azzar imdewweb jistgħu parzjalment jibqgħu fl-azzar imdewweb u jsiru inklużjonijiet fl-azzar. Minħabba l-punt tat-tidwib għoli ta 'dawn l-inklużjonijiet, jistgħu jservu bħala ċentri ta' nukleazzjoni mhux omoġenji meta l-azzar imdewweb jissolidifika, u għandhom rwol fl-irfinar tal-istruttura tas-solidifikazzjoni tal-azzar; u minħabba li dawn l-inklużjonijiet mhumiex deformati faċilment fit-temperatura tal-irrumblar, xorta jżommu forma żgħira sferika jew tal-magħżel, sabiex il-morfoloġija tal-inklużjonijiet fl-azzar tkun tista 'tiġi kkontrollata, u b'hekk tiġi evitata jew tegħleb l-aniżotropija tal-proprjetajiet tal-azzar ikkawżata mill-estensjoni u deformazzjoni ta 'tipi oħra ta' inklużjonijiet (bħal MnS) waqt l-ipproċessar tal-pressjoni sħuna, u tagħmel id-direzzjonijiet lonġitudinali, trasversali u ħxuna tal-proprjetajiet tal-azzar għandhom tendenza li jkunu konsistenti. Dan it-tip ta 'modifika ta' azzar trattat ta 'art rari bħalissa huwa l-aktar kontenut ta' applikazzjoni importanti ta 'addittivi ta' azzar rari.